industrial repair agent > high temperature steel repair agent epoxy compound coating

high temperature steel repair agent epoxy compound coating

BD117 high temperature metal steel repair agent epoxy compound ceramic coating

Product description of our BD117 steel metal high temperature resistant epoxy compound coating repair agent:
It’s the high temperature high performance polymerization metal materials compounded by various alloy material and
modified toughening heat resistant resin.The highest temperature resistance is 300℃,suitable for the repairing of various
carbon steel, alloy steel,stainless steel under the high temperature working condition.Such as fill up casting defects and
repair wear parts.the color after repairing is basically the same as the substrates,with the very high strength and excellent
wear&corrosion resistance and aging resistant properties,can do various mechanical processing together with substrates.

Product index:

product name	physical state	standard packaging	volume (cm3)	operational time limit (25℃)	usable time (25℃)
BD117 high temperature steel metal repair agent epoxy compound ceramic coating	paste	250g/set Two-component	163	45min	24h

color	density (g/cm3)	compressive strength (Mpa) GB1041-2008	shear strength (Mpa) GB7124-2008	bending strength (Mpa) GB1042-1999	hardness （Shore D） ASTM-D-2556	working temperature （℃）
steel	1.53	103	16	53	86	-60～250

How to use:
1.Surface treatment: Do the coarsening treatment on the pending-repair or needing-bonding area,then clean it by cleaning agent.

2.Configuration: According to the mass ratio A:B=4:1 or volume ratio A:B=4:1, make A and B two components mix uniformly,
then use it up within specified operation time limit.

3.Coating: Make the mixed-up material spread coating on the pending-repair areas layer by layer,the first layer should be compacted,make it infiltrate fully with the substrates.
If the following working procedure needs machining,should keep out appropriate machining allowance

4.Curing: Cure for 24 hours at the temperature of 25～30 degree before using,if the temperature is below 15 degree,the curing speed is slow,can’t cure fully,need baking with iodine tungsten lamp or heating it up to the
temperature of 60～80 degree and keeping this temperature for 2 hours with hair dryer after the adhesive
layers initial curing.

Packaging specification:
Two-component,250g/set,8 sets/carton or 16 sets/carton.

Transportation storage:
Sealed storage in the cool and dry place.The warranty period is 24 months.Avoid placing it upside down,
knocking against and transporting it as a non-dangerous product during transportation.